As part of ongoing research to find the most durable battery system, Cadex has performed life cycle tests on nickel-cadmium, nickel-metal-hydride and lithium-ion batteries. All tests were carried out on the Cadex 7000 Series battery analyzers in the test labs of Cadex, Vancouver, Canada. The batteries tested received an initial full-charge, and then underwent a regime of continued discharge/charge cycles (Sony Vaio VGN-FZ battery). The internal resistance was measured with Cadex's OhmTest method, and the self-discharge was obtained from time-to-time by reading the capacity loss incurred during a 48-hour rest period. The test program involved 53 cell phone batteries, of which one per chemistry was chosen for the charts below (Sony VGP-BPS8 battery).
Nickel-cadmium
In terms of life cycling, standard nickel Cadmium is the most enduring battery. Figure 1 illustrates the capacity, internal resistance and self-discharge of a 7.2V, 900mA nickel-cadmium battery with standard cells. Due to time constraints, the test was terminated after 2300 cycles(Sony VGP-BPL9 battery). The capacity remained steady, the internal resistance stayed flat at 75mW and the self-discharge was stable. This battery receives a grade 'A' for almost perfect performance. It should be noted that nickel-cadmium has a moderate energy density, requires periodic full discharges and contains toxic metals(Sony VGP-BPS9 battery).
The ultra-high capacity nickel-cadmium offers up to 60% higher in energy density compared to the standard version at the expense of reduced cycle life. In Figure 2, we observe a steady drop of capacity during the 2000 cycles delivered. At the same time, the internal resistance rises slightly. A more serious degradation is the increase of self-discharge after 1000 cycles (Sony VGP-BPL11 battery).
Nickel-metal-hydride
Figure 3 examines nickel-metal-hydride. We observe good performance at first but past 300-cycles, the readings starts to deteriorate rapidly. One can observe the swift increase in internal resistance and self-discharge after cycle count 700. nickel-metal hydride has a higher energy density than nickel-cadmium and does not contain toxic metals. Some argue that nickel-metal-hydride is an interim step to lithium-ion (Sony VGP-BPL15 battery).
Lithium-ion
In Figure 4 we examine the capacity and internal resistance of a lithium-ion battery. A gentle and predictable capacity drop is observed over 1000 cycles and the internal resistance increases only slightly. Because of low readings, self-discharge has been omitted on this test. lithium-ion offers the highest energy density of the above-mentioned chemistries and contains no toxic metals. Limited discharge current, the need for safety circuits and aging are negative attributes of this battery(Sony VGN-FZ460E battery).
When conducting battery tests in a laboratory, it should be noted that the performance in a protected environment is commonly superior to that in field use. Elements of stress and inconsistency present in everyday use cannot be simulated accurately in the lab. Here are some of the reasons why(Sony VGP-BPS11 battery):
Under a full cycle program, as conducted in this test, nickel-based batteries are not affected by crystalline formation (memory). Memory shortens battery life in everyday use if not properly maintained. Applying a full discharge/charge cycle once a month solves this problem. Nickel-cadmium is more prone to memory than nickel-metal-hydride(SONY VAIO VGN-FZ4000 Battery).
Lithium-ion benefited from a controlled life cycle test because the aspect of aging plays a less significant role. The service life of lithium-ion in real life is a combination of cycle count and aging. All batteries are affected by aging in various degrees(Sony VGP-BPS10 battery).
Another reason why life the lab cycling produced very positive readings is the controlled temperature environment in which the tests were carried out. In true life, the batteries meet much harsher treatment and are often exposed to heat. Furthermore, the batteries in our test were charged with a well-defined charge algorithm. Overcharge was minimized and damaging heat buildup prevented. Low-cost consumer chargers do not always service the battery optimally (Sony VGP-BPS13 battery).
The type of load with which the batteries are discharged also plays a role. The above test consisted of an even DC discharge. Digital equipment loads the battery with heavy current bursts. Tests have shown reduced cycle life when a battery is discharged with sharp current pulses as opposed to DC, even though the delivered end-energy is the same. Cell phones, laptop computers digital cameras are devices that draw such heavy current spikes (Sony Vaio VGN-FZ18M battery).
In some other aspects, however, a lab test may be harder on the battery than actual field use. In our test, each cycle applied a full discharge. The nickel-based packs were drained to 1.0 volt and lithium-ion to 3.0 volts per cell. In typical field use, the discharge before re-charge is normally shallower. A partial discharge puts less strain on the battery, which benefits lithium-ion and to some extent also nickel-metal-hydride. Nickel-cadmium is least affected by delivering full cycles. Manufacturers normally specify the cycle life of lithium-ion at an 80% depth-of-discharge(Sony VGN-FZ61B battery).
What is the best cycling pattern?
I often get asked by the readers, "how deep can a battery be discharged and still achieve maximum service life?" There are no definite answers. Batteries are like us humans. Suppose we ate all the vegetables our mother heaped on our plates and do our daily exercise, would we life longer? Perhaps. But by how much, no one will know. Batteries lose capacity as part of aging, cycling and exposure to heat. Nickel-cadmium also loses capacity due to lack of exercise because of memory(Sony VGN-FZ31E battery).
To maximize service life, satellite batteries are kept at a cool temperature and undergo a very shallow discharge of only 10% before recharge. Nickel-based batteries in space also receive a periodic full discharge. This regime allows ten of thousands of cycles. Closer to earth, the ideal charge/discharge patterns cannot be scheduled; neither is the temperature always perfect. As a result, a replacement will be required sooner or later(Sony VGN-FZ340E battery).
If possible, do not discharge lithium-based batteries too deeply. Instead, recharge more often. Allow a nickel-cadmium battery to fully discharge once every 30 cycles or so. This also applies to nickel-metal-hydride but to a lesser extent. Exact data as to how often a nickel-based battery should be discharged is not available. Neither do we know low long a lithium-ion will last under different depth-of-discharge regimes. Manufacturers typically specify lithium-ion at an 80% depth-of-discharge(Sony VGN-FZ18E battery).